Failure Analysis of The Crack and Leakage of A Cru by Anandkumar Tewari is a document available to read on EtoBox.
This paper analyzes the failure of a crude oil pipeline due to cracks and leakage under CO2-steam flooding in China. Various testing methods revealed that high humidity, oxygen content, and chloride environments led to pit corrosion and stress corrosion cracking (SCC), exacerbated by insufficient nickel content in the pipeline material. The study provides insights into the failure mechanisms and suggests precautions to prevent future fractures.