API RP-571: Metallurgical Failures Overview by glazetm is a document available to read on EtoBox.

This document from API RP-571 discusses various types of mechanical and metallurgical failures that can occur in refinery equipment, including high temperature hydrogen attack (HTHA), temper embrittlement, brittle fracture, wet H2S damage, erosion-corrosion, corrosion fatigue, chloride stress corrosion cracking, and mechanical fatigue. For each type of failure, it describes the appearance of damage, materials affected, typical locations in refineries where it can occur, and other relevant details. The docum