Crystallisation and magnetic behaviour of amorphous and nanocrystalline Fe~81– x – y ~Ni~ x ~Co~ y ~Zr~7~B~12~ alloys by M. Kopcewicz; J. Latuch; T. Kulik is a scholarly article available to read on EtoBox.

What is Crystallisation and magnetic behaviour of amorphous and nanocrystalline Fe~81– x – y ~Ni~ x ~Co~ y ~Zr~7~B~12~ alloys about?

## Abstract The amorphous precursors Fe~81–__x__ –__y__~ Ni~__x__~ Co~__y__~ Zr~7~B~12~ (__x__ = 50, 40, 30, 20; __y__ = 0, 10, 20), prepared by the melt quenching technique, have been characterised in terms of their ability to form nanocrystalline grains on annealing. The crystallisation process was studied in detail using Mössbauer spectroscopy, X‐ray diffraction (XRD) and differential scanning calorimetry measurements. The crystalline phases formed were identified and their transformation versus annealing temperature was followed. Bulk and surface crystallisation of amorphous precursors was compared using conversion electron Mössbauer spectroscopy. The size of nanograins was estimated from the XRD results using the Scherrer formula. The magnetic properties of amorphous and nanocrystalline Fe~81–__x__ –__y__~ Ni~__x__~ Co~__y__~ Zr~7~B~12~ alloys were studied using an unconventional ‘rf‐Mössbauer’ technique. The rf‐Mössbauer technique provides information on the soft magnetic behaviour of alloys. The rf sidebands observed are directly related to magnetostriction and their presence provides a good test for the formation of the nanocrystalline alloy. The rf‐Mössbauer results reveal

Author

M. Kopcewicz; J. Latuch; T. Kulik

Publisher

John Wiley and Sons; Wiley (John Wiley & Sons); John Wiley & Sons Ltd.; Wiley; Wiley - V C H Verlag GmbbH & Co. (ISSN 0031-8965)

Published

2007