Can I read Porosity Effects in Aluminium Alloys on EtoBox?
Porosity Effects in Aluminium Alloys by Satis Mrt is a document available to read on EtoBox.
What is Porosity Effects in Aluminium Alloys about?
This document summarizes a study that used microtomography, image analysis, and finite element analysis to investigate the causes of fatigue fracture in a cast aluminum alloy. Five samples were tested until failure. Porosity was found to be the primary cause of failure, with cracks initiating and propagating from individual pores. Microtomography was used to image the internal porosity, which was then input into finite element models to simulate mechanical response. Pores that caused failure tended to be la