Can I read Temperature Sensing Properties of Upconverted-emission Materials Based on a Fluoroindate Glass Matrix on EtoBox?

Temperature Sensing Properties of Upconverted-emission Materials Based on a Fluoroindate Glass Matrix by G. Lesly Jimenez; Radosław Lisiecki; B. Starzyk; C. Vazquez-Lopez; Magdalena Lesniak; Magdalena Szumera; Patryk Szymczak; Marcin Kochanowicz; Dominik Dorosz is a scholarly article available to read on EtoBox.

What is Temperature Sensing Properties of Upconverted-emission Materials Based on a Fluoroindate Glass Matrix about?

The optical temperature sensing properties of a low-phonon fluoroindate glass co-doped with different trivalent lanthanide ions (IFG:Ln3+/Yb3+, Ln = Er, Tm, and Tm-Ho) were assessed using the fluorescence intensity ratio (FIR) technique. The temperature-dependent upconverted luminescence was carried out in the temperature range between 300 and 583 K using the thermally-coupled energy levels, non-thermally coupled levels, and their additional combinations. The highest relative sensitivity was obtained in the IFG:Tm3+/Yb3+ sample at 355 K (1.4% K−1), from 3F2, 3H4→ 3H6 FIR evaluation, while the maximum absolute sensitivity was found in the IFG:Ho3+/Yb3+ system at 583 K (0.020 K−1), from Tm(1G4→3H6 +3H4→3H6)-Ho(3F4→5I7) FIR assessment. Furthermore, the chromaticity diagram (CIE) evidenced an important change of color when the temperature increased in IFG:Er3+/Yb3+ sample, because this showed an evident transition from green to yellowish. Also, the heating effect caused by 980 nm excitation is negligible in most of the samples. Additionally, their amorphous nature was confirmed by X-ray diffraction and their thermal stability was evaluated using differential thermal analysis resulting

Author

G. Lesly Jimenez; Radosław Lisiecki; B. Starzyk; C. Vazquez-Lopez; Magdalena Lesniak; Magdalena Szumera; Patryk Szymczak; Marcin Kochanowicz; Dominik Dorosz

Publisher

Elsevier BV

Published

2023

Language

EN