Modulus characteristics during the γ→ε martensitic transformation in Fe–Mn–Si–Cr–N alloys by J.F Wan; S.P Chen; T.Y Hsu; X.L Lei; Y.N Huang is a Physics and Astronomy article available to read on EtoBox.

What is Modulus characteristics during the γ→ε martensitic transformation in Fe–Mn–Si–Cr–N alloys about?

The temperature dependences of internal friction and modulus were measured for the Fe -Mn -Si-Cr -xN alloys. A stable modulus softening of parent was newly observed to associate with the g ! 1 martensitic transformation in the alloys containing certain amount (e.g. . 0.086 mass%) of nitrogen, although the rather strong softening has been always recognized to occur during its reverse transformation. The enhanced strength and the increased stacking fault energy of g matrix by nitrogen alloying are suggested to make contribution to the soft mode.

Who reads Modulus characteristics during the γ→ε martensitic transformation in Fe–Mn–Si–Cr–N alloys?

Author

J.F Wan; S.P Chen; T.Y Hsu; X.L Lei; Y.N Huang

Publisher

Elsevier Science; Elsevier ; Elsevier BV (ISSN 0038-1098)

Published

2004

Language

EN

Field

Physics and Astronomy (Physical Sciences)