Can I read Corrosion Behavior of Ceramic Cup of Blast Furnace Hearth by Liquid Iron and Slag on EtoBox?

Corrosion Behavior of Ceramic Cup of Blast Furnace Hearth by Liquid Iron and Slag by Yanglong Li; Shusen Cheng; Zhifeng Wang is a Engineering article available to read on EtoBox.

What is Corrosion Behavior of Ceramic Cup of Blast Furnace Hearth by Liquid Iron and Slag about?

## Abstract Three kinds of sample bricks of ceramic cups for blast furnace hearth were studied by dynamic corrosion tests based on different corrosion systems, i.e., liquid iron system, liquid slag system and liquid iron–slag system. Considering the influence of temperature and sample rotational speed, the corrosion profiles and mass loss of the samples were analyzed. In addition, the microstructure of the corroded samples was observed by optical microscope (OM) and scanning electron microscope (SEM). It was found that the corrosion profiles could be divided into iron corrosion region, slag corrosion region and iron–slag corrosion region via corrosion degree after iron–slag corrosion experiment. The most serious corrosion occurred in iron–slag corrosion region. This is due to Marangoni effect, which promotes a slag film formed between liquid iron and ceramic cup and results in local corrosion. The corrosion of the samples deepened with increasing temperature of liquid iron and slag from 1,623 K to 1,823 K. The variation of slag composition had greater influence on the erosion degree than that of rotational speed in this experiment. Taking these results into account the ceramic cup

Who reads Corrosion Behavior of Ceramic Cup of Blast Furnace Hearth by Liquid Iron and Slag?

Author

Yanglong Li; Shusen Cheng; Zhifeng Wang

Publisher

Walter de Gruyter GmbH

Published

2016

Language

EN

Field

Engineering (Physical Sciences)