Can I read Welding Cracks: Main Crack Types on EtoBox?

Welding Cracks: Main Crack Types by hemnath is a document available to read on EtoBox.

What is Welding Cracks: Main Crack Types about?

Cracks can form during welding in several main types: solidification cracks occur as the weld metal solidifies; hydrogen induced cracks are caused by absorbed hydrogen gas during welding; lamellar tearing results from the formation of hard and brittle zones in the heat affected metal; and reheat cracks appear after welding due to subsequent heating of the weld.