Can I read CrN/CrCN Coating Cavitation Erosion Study on EtoBox?

CrN/CrCN Coating Cavitation Erosion Study by Cihan Erdem is a document available to read on EtoBox.

What is CrN/CrCN Coating Cavitation Erosion Study about?

The study investigates the cavitation erosion resistance of a CrN/CrCN multilayer coating on X6CrNiTi18-10 stainless steel. Results indicate that while the coating increases the incubation period for erosion, the cumulative mass loss is greater than that of the uncoated steel, primarily due to brittle fracture and delamination. The findings suggest that the CrN/CrCN coating is not adequately resistant to high-velocity impacts from cavitation, leading to accelerated degradation.