Pit evolution around the fusion line of a NiCrMoV steel welded joint caused by galvanic and stress-assisted coupling corrosion by Shuo Weng & Yuhui Huang & Fuzhen Xuan & Fuqian Yang is a book available to read on EtoBox.
- Author
- Shuo Weng & Yuhui Huang & Fuzhen Xuan & Fuqian Yang
- Publisher
- Royal Society of Chemistry
- Published
- 2018
- Language
- EN
More by Shuo Weng & Yuhui Huang & Fuzhen Xuan & Fuqian Yang
Browse all works by Shuo Weng & Yuhui Huang & Fuzhen Xuan & Fuqian Yang
Similar books
- Galvanic Corrosion of Duplex Corrosion-resistant Steel Rebars Under Carbonated Concrete Conditions — Jinyang Jiang & Hong-yan Chu & Yao Liu & Danqian Wang & Dong Guo & Wei Sun
- Corrosion Behaviour of Welded Low-carbon Steel in the Arctic Marine Environment — Yoo Youl Choi & Myung Hyun Kim
- Stress Corrosion Of Welded Materials:evaluation And Control
- Influence of the Ultrasonic Surface Rolling Process on Stress Corrosion Cracking Susceptibility of High Strength Pipeline Steel in Neutral pH Environment — Bingying Wang & Yu Yin & Zhiwei Gao & Zhenbo Hou & Wenchun Jiang (2017)
- Irradiation-Assisted Stress Corrosion Cracking (presentation slides) (2003)
- Recommended Practice for Radiographic Examination of Fusion Welded Joints: Part 3: Fusion Welded Circumferential Joints in Steel Pipes of Up to 50 Mm Wall Thickness [Withdrawn: Replaced with ISO 17636] — ISO/TC 44/SC 5 Testing and inspection of welds (1984)